3M 7333 Impact-Resistant Structural Adhesive, 200 Ml, Cartridge, Liquid, Off-White/Silver, Very Slight Acrylic; SKU#: 7333

$93.52

3M™ impact-resistant structural adhesive (IRSA) is formulated for true automotive OEM specified structural bonding applications, excellent for collision absorption in steel structures and advanced lightweight aluminum alloys. This two-part epoxy adhesive delivers extended worktimes - up to 1 hr - and can be rapidly heat-cured. The adhesive changes from silver to purple as the adhesive cures. Engineered to withstand higher impact vs traditional bonding adhesives, 3M™ impact-resistant structural adhesive (IRSA) is excellent for OEM specified automotive structural applications. It adheres to properly prepared automotive substrates including mild steel, high-strength steel and aluminum, vital as OEMs strive to achieve high-strength in increasingly lightweight structures. This two-part epoxy adhesive is recommended for all weld-bonded and rivet-bonded joints when specified by an OEM. It provides an extended work time - up to one hr - and cures rapidly with heat (30 min at 80 deg C). Adhesive applies in a silver color and changes to purple as it cures, indicating when the curing process has begun. 3M™ IRSA is designed to absorb collision energy forces and delivers increased torsional rigidity for OEM specified automotive structures. It allows for spot-welding (form squeeze-type) in an uncured state, typically up to 3 hr after application. Properly applied adhesive will seal joints completely and perform when exposed to very hot and cold temperatures. 3M™ impact-resistant structural adhesive is available in 200 mL cartridges.

3M™ Impact-Resistant Structural Adhesive, 200 mL Net Content, Cartridge Container, Composition: 4,4'-Isopropylidenediphenol-Epichlorohydrin Polymer, Synthetic Rubber, 1,4-Bis ((2,3-Epoxypropoxy) Methyl) Cyclohexane, 3-(Trimethoxysilyl) Propyl Glycidyl Ether, Benzoic Acid, C9-C11-Branched Alkyl Esters, Inorganic Filler, Treated Filler, Treated Inorganic Filler, Phenolphthalein, Liquid Form, Off-White/Silver, Very Slight Acrylic Odor/Scent, 24 hr Curing Time, 200:100 Mixing Ratio, 1.18 Specific Gravity, 1 g/L VOC, 100000 to 500000 cPs Viscosity, 35 MPa Tensile Strength, Applicable Materials: Aluminum, Steel

3M™ impact-resistant structural adhesive (IRSA) is formulated for true automotive OEM specified structural bonding applications, excellent for collision absorption in steel structures and advanced lightweight aluminum alloys. This two-part epoxy adhesive delivers extended worktimes - up to 1 hr - and can be rapidly heat-cured. The adhesive changes from silver to purple as the adhesive cures. Engineered to withstand higher impact vs traditional bonding adhesives, 3M™ impact-resistant structural adhesive (IRSA) is excellent for OEM specified automotive structural applications. It adheres to properly prepared automotive substrates including mild steel, high-strength steel and aluminum, vital as OEMs strive to achieve high-strength in increasingly lightweight structures. This two-part epoxy adhesive is recommended for all weld-bonded and rivet-bonded joints when specified by an OEM. It provides an extended work time - up to one hr - and cures rapidly with heat (30 min at 80 deg C). Adhesive applies in a silver color and changes to purple as it cures, indicating when the curing process has begun. 3M™ IRSA is designed to absorb collision energy forces and delivers increased torsional rigidity for OEM specified automotive structures. It allows for spot-welding (form squeeze-type) in an uncured state, typically up to 3 hr after application. Properly applied adhesive will seal joints completely and perform when exposed to very hot and cold temperatures. 3M™ impact-resistant structural adhesive is available in 200 mL cartridges.

3M™ Impact-Resistant Structural Adhesive, 200 mL Net Content, Cartridge Container, Composition: 4,4'-Isopropylidenediphenol-Epichlorohydrin Polymer, Synthetic Rubber, 1,4-Bis ((2,3-Epoxypropoxy) Methyl) Cyclohexane, 3-(Trimethoxysilyl) Propyl Glycidyl Ether, Benzoic Acid, C9-C11-Branched Alkyl Esters, Inorganic Filler, Treated Filler, Treated Inorganic Filler, Phenolphthalein, Liquid Form, Off-White/Silver, Very Slight Acrylic Odor/Scent, 24 hr Curing Time, 200:100 Mixing Ratio, 1.18 Specific Gravity, 1 g/L VOC, 100000 to 500000 cPs Viscosity, 35 MPa Tensile Strength, Applicable Materials: Aluminum, Steel

Applicable Materials: Aluminum, Steel

Color: Off-White/Silver

Composition: 4, 4'-Isopropylidenediphenol-Epichlorohydrin Polymer, Synthetic Rubber, 1, 4-Bis ((2, 3-Epoxypropoxy) Methyl) Cyclohexane, 3-(Trimethoxysilyl) Propyl Glycidyl Ether, Benzoic Acid, C9-C11-Branched Alkyl Esters, Inorganic Filler, Treated Filler, Treated Inorganic Filler, Phenolphthalein

Container Type: Cartridge

Curing Time: 24 hr

Form: Liquid

Mixing Ratio: 200:100

Net Content: 200 mL

Odor/Scent: Very Slight Acrylic

Specific Gravity: 1.18

Tensile Strength: 35 MPa

VOC Content: 1 g/L

Viscosity: 100000 to 500000 cPs